將 Zn 和 Y 元素以原子比為 6:1 的形式加入 AM50 合金中, 并采用金屬型鑄造成形, 利用 OM, SEM, EDS, XRD, 熱分析法及拉伸實驗研究了 AM50-x(Zn, Y) (x=0, 2, 3, 4, 5, 質量分數(shù), %)合金的顯微組織、凝固行為及力學性能. 結果表明: 向 AM50 合金中按原子比為 6 的形式加入 Zn 和 Y元素后, 組織得到明顯細化, 組織中并未形成 Mg3Zn6Y 準晶相, 而形成了顆粒狀的 Al6YMn6相和細小的 Al2Y 相, 其中 Al6YMn6相尺寸隨著 Zn 和 Y元素含量的增加而增大; 當 x≥3 時, 在組織中 β 相的周圍逐漸形成層片狀的 Φ-Mg21(Zn, Al)17相, 且其數(shù)量逐漸增加. 熱分析結果表明, Φ-Mg21(Zn,?Al)17相約在 354 ℃通過包晶反應形成, 其中 α-Mg 和 β 相析出溫度隨著 x 的增加而降低. 由于 Al6YMn6相、Al2Y 相和 Φ-Mg21(Zn, Al)17相的形成, 使得 β 相的尺寸減小、數(shù)量減少; 當 x=4 時, 合金組織最為細小, 且合金力學性能達到最優(yōu), 其抗拉強度、屈服強度和伸長率分別為 206.63 MPa, 92.50?MPa 和 10.04%.
As the lightest metallic structural material, magnesium alloys were widely used in automotive,?aerospace, electronic equipment and other fields. Among commercial magnesium alloys, AM series were?commonly used due to excellent ductility and energy absorption. However, their relatively poor strength greatly?restricted their extended use. In order to improve mechanical properties of AM50 alloy, the Zn and Y elements?were added into the AM50 alloy in the form of atomic ratio of 6:1 by the permanent mold casting. The?microstructure, solidification behavior and mechanical properties of AM50-x(Zn, Y) (x=0, 2, 3, 4, 5, mass?fraction, %) alloys were investigated by OM, SEM, EDS, XRD, thermal analysis and tensile tests. The results?indicated that addition of Zn and Y elements with an atomic ratio of 6:1 to AM50 alloy, the microstructures were?obviously refined, and the quasicrystal I-Phases (Mg3Zn6Y) cannot form. In addition, the granular Al6YMn6 phase?and fine Al2Y phase were formed in the microstructure, and the size of Al6YMn6 phase increased with increasing?the Zn and Y content. The Φ-Mg21(Zn, Al)17 phase with lamellar structure was formed around β phase when x≥3,?and its amount increased with increasing the Zn and Y addition. Thermal analysis results show that the Φ-Mg21(Zn,?Al)17 phase was formed at 354 ℃ by the peritectic reaction, in which the precipitation temperatures of α-Mg and β?phase were decreased with the increase of x content. Due to the formation of Al6YMn6, Al2Y and Φ-Mg21(Zn,?Al)17 phases, the size and amount of the β phase was decreased. For AM50-4 (Zn, Y) alloy, the microstructure was?greatly refined, and the ultimate tensile strength, yield strength and elongation of the alloy reached to the?maximum, 206.63 MPa, 92.50 MPa and 10.04%, respectively.
作為值得信賴的合作伙伴和高品質金屬合金的半成品供應商，艾荔艾擁有完善的服務體系和專業(yè)的團隊。在同客戶交易的過程中，我們力求根據(jù)不同的應用需求將我們的產(chǎn)品做到精益求精。針對當前和未來的市場需求，艾荔艾致力于為客戶提供最佳的金屬材料解決方案。
AILIAI
has been a reliable partner and supplier of sophisticated and high-quality
semi-finished products maed of alloys. In dialogue with our customers, we
optimise our products to meet the specific application requirements. AILIAI
develops the best alloy material solutions for current and future
challenges.
獲取更多我們供應的合金和服務信息，請致電086-021-67660801或發(fā)電子郵件[email protected]聯(lián)系我們，您也可以通過微博，微信，領英，XING，臉書和推特與我們互動。
For
more information on the alloys and services that we supply,?call
us?at
086-021-67660801 or email us at [email protected]. You can also get in touch
on social media, we are constantly active on?Weibo,?Weixin,?LinkedIn,?XING, Facebook?and?Twitter.