研究鐵鎳基高溫合金GH2984在700~750 ℃蠕變期間的顯微組織演變及其對(duì)性能的影響。
700~750 ℃GH2984合金的蠕變變形機(jī)制Rupture mechanism of GH2984 crept attemperature between 700-750 ℃研究鐵鎳基高溫合金GH2984在700~750 ℃蠕變期間的顯微組織演變及其對(duì)性能的影響。結(jié)果表明：在(700 ℃，300 MPa)蠕變條件下，合金持久壽命僅160 h，變形過程中晶界處的應(yīng)力集中并促進(jìn)裂紋的萌生與擴(kuò)展是造成合金失效的主要原因。應(yīng)力降至200 MPa時(shí)，晶粒旋轉(zhuǎn)導(dǎo)致晶界處應(yīng)力集中得到釋放，抑制裂紋萌生并進(jìn)而使合金持久壽命明顯增長。然而，隨著蠕變溫度的增加，晶粒在變形過程中伴隨出現(xiàn)動(dòng)態(tài)再結(jié)晶。這一現(xiàn)象雖然使得合金持久塑性有所增加，但晶粒加工硬化程度較低造成合金持久壽命明顯縮短。
The microstructure evolution and its effect on the properties of GH2984 alloy between 700 and 750 ℃ were investigated. The results show the rupture life is only about 160 h when the alloy was crept at 700℃ and 300MPa. The stress concentration and consequently crack nucleation and propagation are the main reason for failure of the alloy. When the stress decreases, the stress concentration is released by the grain rotation. It inhibits the crack nucleation and thus extends the alloy rupture life obviously. However, accompanied with the grain deformation proceeding, the dynamic recrystallization occurs when the creep temperature increases. This leads to the increases of the alloy creep ductility, but decreases the alloy rupture life because of the lower work hardening extent.
作為值得信賴的合作伙伴和高品質(zhì)金屬合金的半成品供應(yīng)商，艾荔艾擁有完善的服務(wù)體系和專業(yè)的團(tuán)隊(duì)。在同客戶交易的過程中，我們力求根據(jù)不同的應(yīng)用需求將我們的產(chǎn)品做到精益求精。針對(duì)當(dāng)前和未來的市場(chǎng)需求，艾荔艾致力于為客戶提供最佳的金屬材料解決方案。
AILIAI has been a reliable partner and supplier of sophisticated and high-quality semi-finished products maed of alloys. In dialogue with our customers, we optimise our products to meet the specific application requirements. AILIAI develops the best alloy material solutions for current and future challenges.
獲取更多我們供應(yīng)的合金和服務(wù)信息，請(qǐng)致電086-021-67660801或發(fā)電子郵件[email protected]聯(lián)系我們，您也可以通過微博，微信，領(lǐng)英，XING，臉書和推特與我們互動(dòng)。
For more information on the alloys and services that we supply,?call us?at 086-021-67660801 or email us at [email protected]. You can also get in touch on social media, we are constantly active on?Weibo,?Weixin,?LinkedIn,?XING, Facebook?and?Twitter.