熱加工工藝對(duì)BTi-6431S鈦合金厚板組織與性能的影響
發(fā)布人：上海艾荔艾合金股份有限公司www.shailiai.cn
更新時(shí)間：2016-01-06
研究?jī)煞N熱加工工藝對(duì)BTi-6431S高溫鈦合金厚板顯微組織和力學(xué)性能的影響。
熱加工工藝對(duì)BTi-6431S鈦合金厚板組織與性能的影響Effect of hot working process on microstructure and properties of BTi-6431S titanium alloy plate研究?jī)煞N熱加工工藝對(duì)BTi-6431S高溫鈦合金厚板顯微組織和力學(xué)性能的影響。結(jié)果表明，(α+β)軋制的厚板組織類型為類似于等軸的兩相區(qū)加工組織，β軋制的該合金厚板的顯微組織為典型的細(xì)片狀魏氏組織，該組織厚板的室溫和高溫強(qiáng)度明顯高于α+β軋制厚板的，而塑性稍低；該合金厚板在650 ℃時(shí)具有較高的高溫瞬時(shí)強(qiáng)度，可用于宇航工業(yè)650 ℃短時(shí)用結(jié)構(gòu)件的制作。
The effects of two hot working processes on microstructure and properties of BTi-6431S high temperature titanium alloy plate were studied. The results show that the microstructure of plate in α+β rolling is similar to equiaxed two-phase working microstructure, and the microstructure in β rolling is typical fine lamellar Widmannstaetten structure. The strengths in β rolling at room temperature and high temperature are obviously higher than those in α+β rolling, while the ductility of plate in β rolling is slightly lower. The plates have higher high-temperature transient strength at 650 ℃ and can be used to make short time structure components at 650 ℃ for aerospace industry.
作為值得信賴的合作伙伴和高品質(zhì)金屬合金的半成品供應(yīng)商，艾荔艾擁有完善的服務(wù)體系和專業(yè)的團(tuán)隊(duì)。在同客戶交易的過(guò)程中，我們力求根據(jù)不同的應(yīng)用需求將我們的產(chǎn)品做到精益求精。針對(duì)當(dāng)前和未來(lái)的市場(chǎng)需求，艾荔艾致力于為客戶提供最佳的金屬材料解決方案。
AILIAI has been a reliable partner and supplier of sophisticated and high-quality semi-finished products maed of alloys. In dialogue with our customers, we optimise our products to meet the specific application requirements. AILIAI develops the best alloy material solutions for current and future challenges.
獲取更多我們供應(yīng)的合金和服務(wù)信息，請(qǐng)致電086-021-67660801或發(fā)電子郵件[email protected]聯(lián)系我們，您也可以通過(guò)微博，微信和領(lǐng)英與我們互動(dòng)。
For more information on the alloys and services that we supply,?call us?at 086-021-67660801 or email us at [email protected]. You can also get in touch on social media, we are constantly active on?Weibo,?Weixin?and?LinkedIn.