通過Jominy末端淬火實(shí)驗(yàn)研究2124鋁合金的淬透性。利用溫度數(shù)據(jù)采集、布氏硬度檢測、差示量熱法（DSC）和透射電子顯微鏡（TEM）等手段分析淬火冷卻速率對時(shí)效后第二相析出行為的影響。
基于末端淬火試驗(yàn)2124鋁合金的淬透性Hardenability of 2124 aluminum alloy based on?Jominy end quench test通過Jominy末端淬火實(shí)驗(yàn)研究2124鋁合金的淬透性。利用溫度數(shù)據(jù)采集、布氏硬度檢測、差示量熱法（DSC）和透射電子顯微鏡（TEM）等手段分析淬火冷卻速率對時(shí)效后第二相析出行為的影響。結(jié)果表明：Jominy末端淬火2124鋁合金室溫水淬硬度下降小于10%的淬透深度大約為50 mm，該位置處合金在222.7~350.0 ℃溫度區(qū)間的平均淬火冷卻速率大于2.0 ℃/s；較低的淬火冷卻速率致使過飽和的溶質(zhì)原子和空位損失，導(dǎo)致時(shí)效析出相變驅(qū)動(dòng)力不足，顯著削弱了時(shí)效強(qiáng)化效果。
The hardenability of 2124 aluminum alloy was investigated by means of Jominy end quench test. The effects of cooling rate on ageing precipitation and strengthening behavior were analyzed by temperature data acquisition, Brinell hardness measurement, differential scanning calorimetry (DSC) and transmission electron microscopy (TEM) observation. The results show that the hardening depth with hardness loss below 10% of 2124 alloy Jominy specimen quenched by room temperature water is approximately 50mm where the average cooling rate through the temperature range from 222.7 ℃ to 350.0 ℃ is above 2.0 ℃/s. The age hardening response of 2124 alloy is obviously weakened at slower quenching rate, which is caused by the loss of vacancies and solutes.
作為值得信賴的合作伙伴和高品質(zhì)金屬合金的半成品供應(yīng)商，艾荔艾擁有完善的服務(wù)體系和專業(yè)的團(tuán)隊(duì)。在同客戶交易的過程中，我們力求根據(jù)不同的應(yīng)用需求將我們的產(chǎn)品做到精益求精。針對當(dāng)前和未來的市場需求，艾荔艾致力于為客戶提供最佳的金屬材料解決方案。
AILIAI has been a reliable partner and supplier of sophisticated and high-quality semi-finished products maed of alloys. In dialogue with our customers, we optimise our products to meet the specific application requirements. AILIAI develops the best alloy material solutions for current and future challenges.
獲取更多我們供應(yīng)的合金和服務(wù)信息，請致電086-021-67660801或發(fā)電子郵件[email protected]聯(lián)系我們，您也可以通過微博和微信和我們互動(dòng)。
For more information on the alloys and services that we supply,?call us?at 086-021-67660801 or email us at [email protected]. You can also get in touch on social media, we are constantly active on?Weibo?and?Weixin.