(2) 化學(xué)成分:暫時(shí)不對(duì)外公布。

(3) 力學(xué)性能
?1) 沖擊吸收能量：溫度 20°C/300°C/600°C/650°C/700°C, 沖擊吸收能 65.5J/101J/235J/294J/294J。
?2) 鋼的耐回火性: 回火溫度100°C /200°C/300°C/400°C /450°C/500°C/525°C/550°C/575°C/580°C/600°C/620°C /640°C/650°C/675°C/680°C/700°C。硬度52HRC/52HRC/48HRC/46HRC/46HRC/43HRC/45HRC/45HRC/43HRC/43HRC/40HRC/39HRC/37HRC/37HRC/32HRC/

30HRC/28HRC
?3) 熱加工性能: 溫度 800°C/900°C/1000°C/110o°C/1200°C,抗拉強(qiáng)度162.3MPa /145.9MPa/75.4MPa/41.76MP3/27.09MPa, 伸長(zhǎng)率 39.7%/49.6%/ 59.1%/ 74.9%/ 77.7%。
?4) 拉伸性能:溫度25°C/300°C/600°C/650°C/700°C, 抗拉強(qiáng)度 1395MPa /1291MPa/886MPa/620MPa/356MPa; 屈服強(qiáng)度 1236MPa/ 1073MPa/ 741MPa/ 520MPa/290MPa; 伸長(zhǎng)率17.3%/17.4%/26%/30.3%/42%;斷面收縮率 61%/66.4%/84.7%/90.2%/95.1%
(4) 熱加工規(guī)范:加熱溫度1150~1180°C, 開(kāi)始溫度1150~1180,終止溫度≥930°C

?(5) 淬火、回火規(guī)范:淬火溫度 900 ~920°C, 在20 ~60°C 的油中冷卻到室溫, 硬度 42 -44HRC.回火溫度 560 ~580°C, 硬度 40~42HRC
(6) 典型應(yīng)用舉例:用于大截面熱鍛模具、輥鍛模具。